PRODUCT DESCRIPTION Hot Sale Lead Alloy Anode Pb-Ca-Sn Alloy and Multi-Alloy for Copper Cobalt Nickel metal Hydrometallurgy Electrowinning with Customized size Howah Lead dioxide electrode has low resistivity, good chemical stability, corrosion resistance, good electrical conductivity, can be...
PRODUCT DESCRIPTION
Howah Lead dioxide electrode has low resistivity, good chemical stability, corrosion resistance, good electrical
conductivity, can be through the large current characteristics, with three-dimensional structure coating (precious
metal oxides + alpha PbO2 + beta PbO2), greatly enhanced the adhesion strength of the coating.Widely used in all
kinds of organic electrolytic preparation and sewage treatment and the process of preparing high pure water,
application field is very wide.
FEATURES
* Superconductivity
* Easy installation
* Various size for choice
* Stable and Economy
* Corrosion Resistance
* Good chemical stability
CONSTRUCTION AND PHYSICAL PROPERTIES
Lead dioxide anode current was used as the underlying material basically has: platinum group metal and its oxide,
tin, antimony oxide compound iridium tantalum oxide layer etc.Usually by surface active layer deposition method.
1.Substrate Metal Chemical Composition:
Grade | N | C | H | Fe | O | Ti |
Gr1 | 0.03 | 0.08 | 0.015 | 0.20 | 0.18 | bal |
Gr2 | 0.03 | 0.05 | 0.015 | 0.30 | 0.25 | bal |
Substrate Metal Mechanical Properties:
Grade | Tensile strength(min) | Yield strength(min) | Elongation (%) | ||
ksi | MPa | ksi | MPa | ||
Gr1 | 35 | 240 | 25 | 170 | 30 |
Gr2 | 50 | 345 | 40 | 275 | 30 |
2. MMO Coating: lead oxide (PbO2)
Coating | Oxygen revolution potential | Suitable working environment |
lead oxide (PbO2) | <1.75V | Solution not contain Cl-, PH=7, High COD |
3. Working Parameters for lead oxide (PbO2) Coating:
Current density | Temperature | Chlorine concentration | Polarity reversal | Reversal frequency |
<5000A/m2 | 40-60°C | - | suitable | 2-4 hours |
4. Design Sizes:
Application | Sewage Treatment Inorganic chemical Water electrolysis system |
Common sizes | Custom-made size available (sample size 100*100mm) |
STANDARD
ASTM B843-1995,GB/T21448-2008,GB/T17731-2009
QUALITY CONTROL
Quality Control in our foundry begins on the foundry floor, where the first line of inspection is the casting and
molding crew, our lab technicians inspectors and managers completes the quality team. Our quality control staff
carefully monitors raw material, core materials,packaging and all aspects of production.
APPLICATION
Related Products
PAYMENT & SHIPMENT
Welcome to buy high quality hot sale lead alloy anode pb-ca-sn alloy and multi-alloy for copper cobalt nickel metal hydrometallurgy electrowinning with customized size from Howah Industry which is well-known as one of the leading manufacturers and suppliers in China. Constantly introducing advanced technology and equipment, our factory is able to offer you anode products with extremely high electrochemical performance, large capacity and lasting service time at competitive price.
If you are interested in our products or you have any questions ,please contact with me,i am Erin,i will give you the best servive,
Emai:erin@howahmetal.com
What up:+8615029035402
Skype:Erin Wang